SMC/BMC Resin


Product family of MERICAN

Product Name Type Viscosity cPs @25℃ Tensile str.MPa HDT℃ Remarks
MERICAN 9016L Halogen free Ortho 40-60 75 L.O.I. = 36(Resin casting), 50(FRP laminate). UL-94 V-0, BS476-6 class 0, DIN 5510 S4/ST2/SR2 when ATH added
MERICAN 9015 TCEP filled Ortho 230-370 82 L.O.I. = 27(Resin casting), 32(FRP laminate), light transmitting
MERICAN 9709SY Brominated Ortho 300-400 75 L.O.I. = 28(Resin casting), 32(FRP laminate), UL-94 V-0
MFE 707A Brominated VE 300-450 106-110 L.O.I. = 35(Resin casting), 40(FRP laminate), ASTM E-84 Class A, UL-94 V-0, excellent electrical performance
MFE 707 Halogen free VE 300-450 108-115 L.O.I. = 28(Resin casting), 38(FRP laminate). UL-94 V-0, BS476-6 class 0, DIN 5510 S4/ST2/SR2 when ATH added
Product Name

Type

Halogen free Ortho

Viscosity cPs @25℃

40-60

Tensile str.MPa

HDT℃

75

Type

TCEP filled Ortho

Viscosity cPs @25℃

230-370

Tensile str.MPa

HDT℃

82

Type

Brominated Ortho

Viscosity cPs @25℃

300-400

Tensile str.MPa

HDT℃

75

Type

Brominated VE

Viscosity cPs @25℃

300-450

Tensile str.MPa

HDT℃

106-110

Type

Halogen free VE

Viscosity cPs @25℃

300-450

Tensile str.MPa

HDT℃

108-115

Product Name Type Viscosity cPs @25℃ Tensile str.MPa HDT℃ Remarks
MERICAN 9016L Halogen free Ortho 40-60 75 L.O.I. = 36(Resin casting), 50(FRP laminate). UL-94 V-0, BS476-6 class 0, DIN 5510 S4/ST2/SR2 when ATH added
MERICAN 9015 TCEP filled Ortho 230-370 82 L.O.I. = 27(Resin casting), 32(FRP laminate), light transmitting
MERICAN 9709SY Brominated Ortho 300-400 75 L.O.I. = 28(Resin casting), 32(FRP laminate), UL-94 V-0
MFE 707A Brominated VE 300-450 106-110 L.O.I. = 35(Resin casting), 40(FRP laminate), ASTM E-84 Class A, UL-94 V-0, excellent electrical performance
MFE 707 Halogen free VE 300-450 108-115 L.O.I. = 28(Resin casting), 38(FRP laminate). UL-94 V-0, BS476-6 class 0, DIN 5510 S4/ST2/SR2 when ATH added
Product Name

Type

Halogen free Ortho

Viscosity cPs @25℃

40-60

Tensile str.MPa

HDT℃

75

Type

TCEP filled Ortho

Viscosity cPs @25℃

230-370

Tensile str.MPa

HDT℃

82

Type

Brominated Ortho

Viscosity cPs @25℃

300-400

Tensile str.MPa

HDT℃

75

Type

Brominated VE

Viscosity cPs @25℃

300-450

Tensile str.MPa

HDT℃

106-110

Type

Halogen free VE

Viscosity cPs @25℃

300-450

Tensile str.MPa

HDT℃

108-115

Product Name Type Viscosity cPs @25℃ Tensile str.MPa HDT℃ Remarks
MFE 707 Halogen free VE 300-450 108-115 L.O.I. = 28(Resin casting), 38(FRP laminate). UL-94 V-0, BS476-6 class 0, DIN 5510 S4/ST2/SR2 when ATH added
MERICAN 9190P Ortho 100-200 80-100 Low viscosity, long gel time
MERICAN 30-200P VE 150-250 105-110 Longer gel time than MFE 11VP, for large FRP infusion
MERICAN 9406TP Iso 300-500 90-100 Thixotropic version for hand lay-up and spray up
MERICAN 9406VP Iso 180-220 85-95 low viscosity, peak exotherm and shrinkage for RTM
MERICAN 9709TP Ortho 300-600 75-85 Thixotropic version for hand lay-up and spray up
MERICAN 9709VP Ortho 150-250 75-85 Low viscosity, peak exotherm and shrinkage for RTM
MFE 11TP BPA-VE 300-500 95-105 Thixotropic version for hand lay-up and spray up
MFE 11VP BPA-VE 150-250 95-105 Low viscosity, peak exotherm and shrinkage for RTM
Product Name

Type

VE

Viscosity cPs @25℃

300-450

Tensile str.MPa

HDT℃

108-115

Type

Ortho

Viscosity cPs @25℃

100-200

Tensile str.MPa

HDT℃

80-100

Type

VE

Viscosity cPs @25℃

150-250

Tensile str.MPa

HDT℃

105-110

Type

Iso

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

90-100

Type

Iso

Viscosity cPs @25℃

180-220

Tensile str.MPa

HDT℃

85-95

Type

Ortho

Viscosity cPs @25℃

300-600

Tensile str.MPa

HDT℃

75-85

Type

Ortho

Viscosity cPs @25℃

150-250

Tensile str.MPa

HDT℃

75-85

Type

BPA-VE

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

95-105

Type

BPA-VE

Viscosity cPs @25℃

150-250

Tensile str.MPa

HDT℃

95-105

Product Name Type Viscosity cPs @25℃ Tensile str.MPa HDT℃ Remarks
MERICAN 3881 Epoxy 1500 190-210 Tera-functional groups, high Tg(220℃), low viscosity, long pot life, fast curing under proper temperature
MERICAN 9709 Ortho 300-500 75 Mid-reactivity
MERICAN 9409 Iso 300-500 115 High reactivity
MERICAN 9406 Iso 300-500 105 Mid-reactivity
MERICAN 9400 Iso 300-500 70-75 Low reactivity
MFE 30-900 BPA-VE 800-1000 105 High reactivity
MFE 722
MFE 711 BPA-VE 250-450 105 Mid-reactivity
Product Name

Type

Epoxy

Viscosity cPs @25℃

1500

Tensile str.MPa

HDT℃

190-210

Type

Ortho

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

75

Type

Iso

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

115

Type

Iso

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

105

Type

Iso

Viscosity cPs @25℃

300-500

Tensile str.MPa

HDT℃

70-75

Type

BPA-VE

Viscosity cPs @25℃

800-1000

Tensile str.MPa

HDT℃

105

Type

Viscosity cPs @25℃

Tensile str.MPa

HDT℃

Type

BPA-VE

Viscosity cPs @25℃

250-450

Tensile str.MPa

HDT℃

105

Product Name Type Viscosity cPs @25℃ Tensile str.MPa HDT℃ Remarks
MERICAN 960 Iso 600-1000 135 High gloss, high reactivity
MERICAN 964 Ortho 1750-2250 138 High gloss, high reactivity
MERICAN 963 Ortho 1350-1850 136 Zero shrinkage, Class A surface
MERICAN 962 Ortho 1350-1850 136 Food grade
MFE 757 Novalac VE 2000-3000 -- Linear shrinkage<0.15%, Tensile, blend and impact strength drop within 10% after 1000h under 150±2℃, service life > 7 years
MFE 755 VE 2000-2600 105 High gloss, low profile
MFE 752 VE 1250-2120 100-105 Low viscosity
Low water content (<0.02%)
MFE 751 VE 2100-3100 110-115 High reactivity & toughness
Product Name

Type

Iso

Viscosity cPs @25℃

600-1000

Tensile str.MPa

HDT℃

135

Type

Ortho

Viscosity cPs @25℃

1750-2250

Tensile str.MPa

HDT℃

138

Type

Ortho

Viscosity cPs @25℃

1350-1850

Tensile str.MPa

HDT℃

136

Type

Ortho

Viscosity cPs @25℃

1350-1850

Tensile str.MPa

HDT℃

136

Type

Novalac VE

Viscosity cPs @25℃

2000-3000

Tensile str.MPa

HDT℃

--

Type

VE

Viscosity cPs @25℃

2000-2600

Tensile str.MPa

HDT℃

105

Type

VE

Viscosity cPs @25℃

1250-2120

Tensile str.MPa

HDT℃

100-105

Type

VE

Viscosity cPs @25℃

2100-3100

Tensile str.MPa

HDT℃

110-115